INTERNAL CORRESPONDENCE
CHEMICALS AND PLASTICS
to (name)
COMPANY LOCATION
E. Eisenhour TEXAS CITY PLANT
DATE
RECEIVED
AU6 081374tL N. WHEELER, J.T
P. O. BOX 471. TEXAS CITY, TEXAS 77590
August 5, 1974
COPY TO
Dr. W. B. Ackart - 312 Dr. C. E. Colwell - 525 Mr. R. L. Frantz Mr. R. E. Graebert - 511 Mr. R. J. Hanna - 511 Mr. F. L. Johnson Mr. R. W. Sesler Mr. G. T. Scott - 501
Dr. A. B. Steele - 501 Mr. G. F. Tacquard *--MrrT. N. rfheel er Dr. N. L. Zutty - 501
SUBJECT Residual VCM Content ofx Suspension Vinyl Resins
Attached in Table I is a summary of the VCM content of the sus pension vinyl resins produced during July, 1974. The data continue to confirm that the continuous stripping of suspension resins since May has resulted in an overall reduction in the residual VCM content of all resin types. Some inconsistencies in the stripping/drying area continue to be observed, particularly with QSAN-7. A detailed tabulation of the resins produced during July is provided in Tables II - V.
RMA/sn Attachment
R. M. Arnold
UCC 038755
ucc
038756
TABLE I REVIEW OF VCM DATA OF SUSPENSION VINYL RESINS
Resin Type Production Period
QSAN-7
June, 1974 July, 1974
QSQH-7
April-May, 1974 July, 1974
QSAH-7
May, 1974 July, 1974
VSJE-10
May, 1974 July, 1974
No. Blends Analyzed
96 88
51 16
20 18
8 14
Z100 ppm 26 22
% Blends 100-500 ppm >1000 ppm
53 9
59 8
0 73 0 88
4 0
05 6 17
50 17
0 50 0 93
13 0
Average VCM, ......-PEP
351 365
400 343
1125 724
511 281
ucc
038757
Blend No.
B-5404 B-5406
II
Jl
B-5408 B-5410 B- 5412 B-5414 B-5416 B-.5418 B-5420 B-5422
II
II
II
B-5424 B-5426 B-5428
II
II
II
B-5430 B-5432 B-5434 B-5436 B-5438 B-5440 B-5444 B-5446 B-5448 B-5450
II
B-5452 B-5454 B-5456
II
11
B-5458 B-5460
TABLE II
ANALYSIS OF SUSPENSION VINYL RESIN QSAN-7 FOR RESIDUAL VCM
Date
7-8 7-9
11
II
11
7-8
II
II
7-10 7-11 7-12 7-16
II
II
II
7-13 11
7-19 11 11
II
7-13
II
7-15 7-16 7-13 7-15
M
7-13 7-15 7-18
11
7-17
II
7-20 11
11
7-18 7-19
Container
900 ' 55252
H
II
II
A CA CB
655
857
826
496
714
532
57100 A
BII 11 CA 11 CB
566
757 57101
It
11 11
A B CA CB
642
711
567
806
883
860
672
825
525
57029 B
II CB
517
649 55392
A
11 B .
II CB
647
302
VCM,
Him..,
167 153
3 177 172 295 425 172 146 600 1558 156 288 485 527
85 121 246
79 22 37 292 244 183 28 176 240 295 264 157 89 106 93 347 109 115 709 62 520
Blend No.
B-5463 B-5465 B-5468 B-5470 B-5473 B-5475 B-5477 B-5478 B- 5480 B-5482 B-5484 B-5486 B-5489 B-5490 B-5492 B-5494 B-5496 B-5499 B-5500 B-5502 B-5504 B-5506 B-5508 B-5510
11
II
It
B-5572 B-5514 B-5516 8-5519 B-5521 B-5522
(1
II
11
B-5524 B-5526 8-5528
'
Date
7-21 7-19
11
11
7-22 7-23 7-20
11
7-22 7-23
11
7-25 7-20 7-21 7-22 7-23 7-24 7-27 7-24
11
11
7-26 7-25
II
11
11
11
II
II
7-26
11
II
7-29
11
11
11
7-27 7-30 7-31
Container
683 765 630 324 729 627 582 345 702 501 286 159 329 841 311 707 565 103 496 768 842 701 295 55257
II
11
II
549 678 301 597 512 57070
11
II
II
548 609 595
A B CA CB
A B CA CB
VCM,
. reel.
135 431 2660 197 1213 122 154 450 95 137 213 269 1837 447 514 "37 323 321 84 324 921
90 167 387 941 1593 237 231 1138 404
34 268
81 86 66 56 77 141 360
ucc
038758
Blend No.
B-5529 B-5531 B-5533 B-5535 B-5537 B-5539 B-554G B-5542 B-5544 B-5546
TABLE II (Continued) ANALYSIS OF SUSPENSION VINYL RESIN QSAN-7 FOR RESIDUAL VCM
Date Container
7-30 7-27 7-28 7-27 7-29
M
7-30 7-1131
8-1
147 327 702 532 631 461
769 780 586
672
VCM ppm
1375 642 183 642 300 153 380 225 254
89
ucc
038759
Blend No.
B-1664 B-1666 B-1668 B-1670 B-1672 B-1674 B-1676 B-1678 B-1680 B-1682 B-1684 8-1686 B-1688 B-1690 B-1692 B-1694 B-1696 B-1698
Date
7-3 7-4 7-5
7-7 7-8 7-9
7-10
7-11
TABLE III ANALYSIS OF SUSPENSION VINYL RESIN QSAH-7 FOR RESIDUAL VCM
Container
________
688 774 679 557 902 695 739 849 300 893 664 460 763 619 695 510 464 373
VCM,
PPPL
1917 515 621 789
1144 548 633 940 79 754 555 328 253 818 787 639 202 1501
ucc
038760
Blend No.
B-796 B-798 B-800 B-802 B-804 B-806 B-808 B-810 B-812 B-814 B-816 B-818 B-820 B-822 B-824 B-826
TABLE IV
ANALYSIS OF SUSPENSION VINYL RESIN QSQH-7 FOR RESIDUAL VCM
Date
7-13-74
II
7-14
II (( II
7-15
II
7-16
IJ
7-17 7-18
II JJ
7-19
11
Container
574 652 826 553 872 845 807 378 861 172 395 865 621 315 566 596
VCM, JSESL 113 376 124
117 309 800 375 242 338 473 226 916 404 293 147 227
ucc
Blend No.
B-530
II II II
B-534
II II
B-542
*1 II
B-544 B-546 B-548 B-550
o>
TABLE V ANALYSIS OF SUSPENSION VINYL RESIN VSJE-10 FOR RESIDUAL VCM
Date
7-12
II <1 ll
7-16
II 11
7-28
II II
7-29 7-31
II II
Container
55238
ll II U
55243
11 II
44004
II II
619 693 805 328
A 8 CA CB A CA CB A B CA
VCM, 2QL 189 298 313 141 427 429 287 287 325 306 358
397 505 238