Document ZBOkxMLqJOpBxwOXpvBR75j1V

886 CHAPTER 42 1950 Guide of brines. Ammonia precipitates calcium and magnesium salts thus clogging the system at restricted points. The addition of caustic soda and sodium dichromate to brine solutions to inhibit corrosion of iron, is a more or less general practice. Sodium sili cate and sodium phosphate are also used at times, but tests indicate they are not as effective as is sodium dichromate. It has been suggested80 that 125 lb of sodium bichromate per 1000 cubic feet of calcium chloride brine, and 200 lb per 1000 cubic feet of sodium chloride brine, be added to inhibit brines; that when salt or calcium chloride is added to "strengthen" brine, sodium dichromate also be added in the amounts shown in Table 7. Refrigerants.. The common refrigerants, except those of the hydro carbon type, will attack the common , metals and alloys if moisture is present. Even a very small amount of water may. cause severe corrosion Table 7. Quantities of Sodium Dicbbomate to be Added to Maintain Initial Concentration Specific Gravity of Brine to be Strengthened 1.16 1.18 1.20 1.22 1.24 1.12 1.14 1.16 1.175 Lb Sodium Dichromate per 100 lb CaCl* Added 0.695 0.621 0.556 0.502 0.455 Lb of Sodium Dichromate per 100 lb NaCl Added 1.79 1.47 1.32 1.18 with certain refrigerants. The amount required need only be sufficient to produce a water film on the metal surface. With the halogenated hydrocarbons, complete elimination of water is much to be desired. Where ammonia is used, copper and its alloys, aluminum and zinc, are attacked especially at elevated temperatures. When sulphur dioxide is used, more than 50 ppm (0.005 per cent) of water , will cause appreciable corrosion of virtually all the common materials. Minimizing Condensate Corrosiveness \ There are four expedients that may be utilized to minimize corrosion in steam condensate systems: (1) treatment of the boiler feedwater so ' as to eliminate deleterious gases entrained with the steam, (2) design of the condensing equipment to minimize dissolution in the condensate of, the deleterious gases entrained with the steam, (3) chemical treatment' of the condensate, (4) use of resistant metals. Boiler Feedwater Treatment. Elimination of oxygen from boiler feed-'' water and, therefore, from the steam developed, can be accomplished either mechanically or chemically. In some steam generating stations,, both expedients are employed. Tests" have indicated that in small low-pressure heating boilers, where the boiler- input contains less than about 50 ppm of carbonate hardness, CoiTbsioii and Water Formed Deposits, Causes and Prevention 887 the COi in the steam can be controlled by adding calcium hydroxide to the boiler. In Fig. 5 are shown the equilibria conditions proposed for boilers operating at pressures lip to about 5 psi gage. This expedient may not be used in higher pressure boilers, because of the possibilities of scale and sludge formations. In the latter, the only method used to date for treating the feedwater consists of removing the alkaline earth salts, i.e., softening, and subsequent acidulation followed by deaeration at tempera tures near the atmospheric boiling point of water.82 Design of Condensing Equipment. In the design of water heaters and comparable types of condensing equipment,!J it is possible to shift the accumulation of non-condensible gases to a location away- from the con densate level and, subsequently, vent these gases to the atmosphere. Fio. 5. Relation of Htdbate/Cabbonate Content in Hard Boileb Wateb and Coi in Steam at About 5 Psi Opebating Pbessube (All analytical values are ppm by weight) Venting an amount of steam equal to about one-half per cent of the total steam entering the condenser is the optimum vent rate. Venting, is of little practical value, when the COj content of the in coming steam is below about 5 ppm. When the steam contains more than 5 ppm, venting provides a means of producing a condensate containing, a minimum of about 3 ppm. However, even as little as 3 ppm of dissolved COj can produce active corrosion if large amounts of condensate are flowing. : Chemical Treatment of Condensate. Condensates containing compara tively large amounts of oil, are practically non-corrosive, due to the pro tective film provided by the oil. When oil is intentionally, added to con densate,14 inadequate, quantities may accelerate rather than decelerate corrosion on those surfaces not covered by the oil. Sodium silicate added to COs-bearing condensate has been shown to decrease, but not entirely prevent, corrosive action. It is not definite whether the protection afforded by silicate solutions is due to the establishment of a protective