Document Bn78Xv6O5gYwr9dX8aQ2eR8J

Monsanto Chemicals _______ ^_______ AROCLORS as Used in Pliolite S-5 Monsanto Technical Bulletin No. P-126 March 1, 1948 Monsanto Chemical Company, $t. Louis 4, Mo. 1 AROCLORS As Usad in Pfioflta S-S The AROCLORS,* chlorinated biphenyl and chlorinated poly phenyls, used as plasticizers and resins impart desired properties to Pliolite S-5 protective and decorative coatings prepared for: Concrete Structures Steel Structures Railway Tank Cars Concrete Floors and Walls Wood and Metal Maritime Equipment These fast drying paints provide excellent protection against adds and alkali, moisture and other commonly known corrosive influences. The formulations of Aioclors and Pliolite S-5 given in this bulletin are in line with good commercial practice and are suggested to the paint manufacturer as practical examples or starting points for pre paring specific paints for use where the important qualities of Aroclor and Pliolite S-5 compositions are desired. * Regilttied in U. S. Patent Office *O I* ? 7 M Tli Infarmatfan cantalnad 1* iMf butltUn It, la aar bt*> fcaawtaif* Iftt* and <***, baft nil m ia|t*t{at mm mada wHhaaft fluanuriw, liaca lha caadMaas mt w ar* bayaad aw canbaL Tba Mantanfta Chamlwl Campaay disclaims any HaWUfy Inewrad In csaimUsn wHh tha ota *1 Ihata data ar tawttfUni, furthamtata, Mfthlny csnftalnad hasafa ahall b* canitruad a racammandattaa H UW any *radact lit **nfllcl wHh axliHac palanh raaaHnff any adiHil ar Ita ata. JZ1 / DSW 150439 STLCOPCB4039880 I. INTRODUCTION The AROCLORS, chlorinated biphenyl and chlorinated polyphenyls, used as plasticizers and resins impart desired properties to Pliolite 8-5, a co-polymer ofbutadiene and styrene developed by Goodyear Tire and Rubber Company, Inc. Pliolite manufactured from natural rubber was used, prior to the last war, largely in paints and coatings requiring good resistance to moisture, adds, alkalies and other corrosive chemicals. During the war natural rubber was unavailable and Goodyear Research developed Pliolite S-5 which has even more outstanding characteristics as a paint base than natural rubber Pliolite. II. PROPERTIES OF PLIOLITE S-S The general and spedfic properties of Pliolite S-5 as given by Goodyear Tire and Rubber Company, Chemical Products Division, Akron, Ohio, are listed in the following Table I: TABLE I. TYPICAL PROPERTIES OF PLIOLITE S-5 General Properties -- Forms . ........................ White resinous powder Light amber milled resin Color of solution. . . . Very pale amber Color of film................ Clear and colorless Odor................................Absence of objectionable "paint" odor Toxicity................................ Non-toxic Chemical Resistance................ Non-oxidizablc, non-saponifiable, highly resistant to moisture, adds> alkalies, soaps and general corrosive influences. Highly resistant to al cohol, very resistant to vegetable, animal and mineral oils and greases. General Physical Qualities . . Thermoplastic, outstanding toughness and adhesion. High degree of flexibility with a minimum amount of plasticizer. Good thermal sta bility; withstands baking. Highly resistant to abrasion and scrubbing. Good aging characteristics; coatings do not oxidize and become brittle- Specific Physical Qualities . Spedfic gravity ................................................................................... 1.03 Index of refraction....................................................................... 1.585 Softening point........................................................................... 500C Tensile strength.................................................................. 1450 p.s.i. Elongation .........................................................................................0.0% Iodine number................... 57.8 Add value....................................................................................Neutral TZT* DSW 150440 STLCOPCB4039881 III. PIGMENTED PLIOLITE S-S PAINT BASES Pigments can be dispersed in Pliolite S-5 Milled Resin by plastic mixing on differential speed two-roll mill or in an internal-type mixer such as the Banburg. For convenient uae Goodyear offen the Pliolite S-5 pigmented bases given in the following Table II: Base No. S5 Resin lA-Sj 2B-S5 5*S5 6-S5 7C-S5 8A-S5 I2-S5 IB-S5 14-S5 15-S5 17-S5 19-S5 35-Ss 38-S5 39C-S5 41A-S5 46B-S5 47-S5 64-S5 65-S5 66-S5 Percent Resin 100% 35% 60% 30% 20% 40% 40% 3>% 40% 3% 3% 80% 30% 80% 40% 40% 35% 50% 30% 25% 40% 70.5% 68A-S5 80-S5 40% 35% TABLE II. PLIOLITE S-5 BASES Percent Pigment or Extender Specific Gravity None............................ ........................................................... ... 65% Titanium Dioxide, Rudle Type.................... ... . 2.02 40% Carbon Black........................ ... ........................................... 70% Zinc Oxide........................................................... . 246 80% Red Lead............................................................................... . 3.60 60% Red Iron Oxide........................ ... ....................................... 60% Zinc Chromate................................................................... 70% Whiting, Precipitated........................................................... . 1.85 60% China Clay........................................................................... 70% Lithopone........................................... ............................... . 2.25 70% Zinc Sulfide ....................................................................... 20% Prussian Blue................................................................... ... 70% Talc, Extra Fine............................................................... 20% C. P. Toluidine Toner....................................................... 60% Yellow Iron Oxide........................ ....................................... 60% C. P. Chrome Green, Medium ........... . 1.89 65% C. P. Chrome Yellow, Medium................................ ... . . 2.30 50% Lampblack........................................................................... . 1.36 70% High Zinc Sulfide Lithopone........................................... 75% Molybdate Orange, Dark................................................... 60%, C. P. Chrome Yellow, Extra Light.................................... . 2,so 7.5% Phthalocyanine Blue........................................................... 1-24 22.0% Magnesium Carbonate....................................................... 60% C. P. Chrome Green, Extra light .................................... 65% Titanium Dioxide, Non-Yellowing, Rutile Type .... . 2,02 DSW 150441 i STLCOPCB4039882 IV. SUGGESTED SOLVENTS FOR AROCLORS AND PLIOLITE S-S COMPOSITIONS Aromatic hydrocarbons, or petroleum naphthas with high aromatic content, are the most satisfactory solvents for Aroclors and Pliolite S-5 coating compositions. Solutions of the compositions in these solvents tolerate dilution with inexpensive petroleum thinness up to about 50 percent by weight of the total solvent content. These solutions are chemically neutral, stable and do not change in viscosity on aging nor do they react with pigments on long storage. The solution viscosity varies somewhat with the solvent used, but in general a 25 percent solution of the paint base in aromatic hydrocarbons has good brushing properties. If a lower solution viscosity is desired, this can be obtained by using the Pliolite milled resin which gives a viscosity of about one-third that of the resin powder. Suggested solvents for Aroclors and Pliolite S-5 compositions are given in Table III. TABLE III. SUGGESTED SOLVENTS FOR AROCLORS AND PLIOLITE S-5 COMPOSITIONS Aromatic Hydrocarbons LV -- Low viscosity solution MV -- Medium viscosity solution HV -- High viscosity solution Pliolite S-5 Concentrations 10% 20% Benzene ............................ Toluene............................ Xylene................................ High Flash Naphtha . . . High Aromatic Content Petroleum Solvents "Apcosol3A................ * lApco Iso 12................ "Solvesso No. 1. . . . * `Solvesso No. 2. . . . *`Solvent No. 2159 . . "Solvent No. 2161 . . Chlorinated Hydrocarbons Carbon tetrachloride . Ethylene dichloride. . Trichloroethylene . . Perchloroethylene . . Monochlorobenzene . Orthodichlorobenzene Tetrachloroethane . . Esters Amyl acetate .... Butyl acetate .... Ethyl acetate .... * * Cellosolve acetate . . Ketones Cyclohexanone . . . Methyl ethyl ketone . Methyl n-amyl ketone Methyl iso-butyl ketone Terpene Hydrocarbons Dipentene................ Turpentine................ Nitro Paraffins 1-Nitropropane . . . LV LV LV LV LV LV LV LV LV LV LV LV LV MV LV MV LV LV LV LV LV LV LV LV LV LV LV LV LV LV LV LV LV LV MV MV LV LV HV MV HV HV MV HV HV LV LV LV LV MV LV LV LV LV LV LV SUPPLIERS `Anderson-Prichard Oil Corp. Standard Oil Co. of N.J. *C. P. Hall Co. Carbide and Carbon Chemical! Corp. DSW 150442 * STLCOPCB4039883 Ia addition to the general information about solvents, Goodyear in their Technical Bulletin 509 present very comprehensive data concerning the selection of solvents and diluents for Pliolite S-5 paints. This is based on the observation that the Kauri-Butanol value has been found to be an excellent guide in choosing solvent mixtures for Pliolite S-5. In general, aromatic hydrocarbon solutions of Pliolite S-5 can be diluted with aliphatic hydrocarbons until die Kauri-Butanol value has been reduced to about 60. In the interest of economics, this serves as a guide in computing the maximum amount of aliphatic hydrocarbon ofknown K-B value that can be used with a given aromatic type solvent ofknown K-B value. Goodyear suggest that the K-B value of the solvent mixture be kept near the 60 value but stress the importance of the factor that during drying the solvent mixture should not become leaner in solvency than this initial value. This can be insured by choosing aliphatic and aromatic solvents possessing approx imately the same boiling range. Due to their lower heat of vaporization, aliphatic hydrocarbons, when mixed with aromatic hydrocarbons of the same boiling range, always evaporate first and consequently such a solvent mixture will become progressively richer in solvent power upon drying. Based on data taken from Circular 709 of the Scientific Section, National Paint, Varnish and Lacquer Association, Washington, D. C., and from bulletins of solvent suppliers, Goodyear in their Bulletin 509 classify a large number of solvents and diluents for Pliolite S-5 as being either very fast, medium or slow drying. This information is highly important particularly since Pliolite S-5 paints dry almost entirely in accordance with the rate of solvent release. V. AROCLOR AND PLIOLITE S-5 PAINTS PREPARATION OF THE PAINTS Pliolite S-5 resin powder or the milled resin, as supplied by Goodyear, is dissolved in a selected solvent or solvent combination to serve as the paint vehicle. Aroclor plasticizers and Aroclor resins, as well as other desired additives, are then incorporated in the vehicle. Pigments are then ground into these solutions by the conventional methods and the coatings are formu lated in the usual manner. Goodyear emphasize that the solution viscosity of their milled Pliolite S-5 resin is approximately one-third that of the resin powder. Consequently the consistency of the finished paint can be varied over a considerable range according to the type of Pliolite resin used as well as by choice of plasticizers and pigments. For convenience in formulating the coatings and because pigment dispersion in the Pliolite S-5 Paint Bases, prepared by plastic milling, is considerably better than can be obtained by wet grinding, the use of the plastic milled pigmented bases (described on page 3) is to be preferred in many formulations and particularly when preparing gloss finishes. Using any of the procedures listed below to facilitate solution, it is standard practice to cut the Pliolite Bases in aromatic hydrocarbon solvents such as toluene, xylene or high flash naphtha for the initial solution. After this operation, petroleum solvents such as mineral spirits are used to make the final dilution of the paint. 1. Agitation by means of a stirring device, or tumbling in a drum or pebble mill until the resin has completely dissolved. 2. A more rapid method is to use simple agitation, as described above, until the material has soft ened. Then pass it through a stone mill or three-roll mill to complete the solution of the resin. 3. Using an internal-type mixer such as a Banbury, a sufficient amount of solvent to form a heavy paste is mixed with the Pliolite S-5 Bases. This mixture is then stirred until the batch is smooth. This operation iB done in three to four hours by keeping the paste sufficiently stiff to develop a temperature of at least t5oF., due to frictional heat. Following this, die batch is diluted until it can be easily transferred to a mixing tank where the balance of the ingredients are added to complete the formulation. W7 DSW 150443 SUGGESTED FORMULATIONS The following general formulation is suggested as a flat vehicle which offers great latitude in the choice of solvents and will enable the paint manufacturer to formulate in accordance with his own ideas and requirements. Ingredients Flat Wall Paint Vehicle Pliolite S'5j Milled Resin ............................................................ Aroclor 5460, Resin........................................................................... Aroclor 1254, Plasticizer................................................................... High Solvency Petroleum Naphtha................................................ Mineral Spirits............................ ... ................................................ Total............................................ Percent by Weight 20 20 10 27.5 100.0 The properties of this vehicle are: Specific Gravity................................................................... 1.03 Weight per Gallon.................................................... 8.59 lbs. Solids Content ................................................................... 50% Viscosity, No. 4 Ford Cup........................................196 seconds This oil-free vehicle was developed for use in the manufacture of flat wall paints by conventional wet grinding procedures. The following flat white wall paint which uses the foregoing described flat vehicle possesses very good brushing and application characteristics: Ingredients Hat Whit* Wall Paint Rutile Titanium Dioxide............................................................... Natural Whiting....................................................... ....................... Asbestine........................................................................................... Flat Vehicle (as described above).................................................... High Solvency Petroleum Naphtha................................................ Mineral Spirits............................................................................... Total........................................ Pounds per 100 Gallons 168 jfii 107 336 99 87 1358 Properties of this flat white are: Weight per Gallon........................................13 pounds (approx.) Solids Content................................................................... 73-93% Consistency................................................... Good for brushing This paint does not contain animal or vegetable drying oils nor rosin. It is non-oxidizing, non-skinning, fast drying, odorless after the solvents have evaporated, non-yellowing, fume resistant, resistant to water and moisture vapor, resistant to soap and alkaline cleansers, resistant to mildew and possesses good aging characteristics. Concrete Floor Enamels The prime requisites for a satisfactory concrete floor enamel include alkali and water resistance, good adhesion, good resistance to abrasion and sufficient hardness to resist marring as well as grinding in of dirt and grit. Although the following enamels are intended primarily for use on concrete floors, they are suggested for general use on concrete, brick and plaster wall surfaces. izi F DSW 150444 STLCOPCB4039885 Ingredients Pliolitc S-5 Base 13............................ Pliolite S-5 Base 38 . . ................. Pliolitc S-5 Base 41A........................ Pliolite S-5 Base 64............................ Aroclor 1254 ........................................ Drying Oil*.................................... ... High Flash Aromatic Naphtha . . . Petroleum Thinner............................ Total Ingredients Pliolite S-5 Base................................ Pliolite S-5 Base 13............................ Pliolite S-5 Base 17............................ Pliolite S-5 Base $4............................ Aroclor 1254........................................ Drying Oil*........................................ High Flash Aromatic Naphtha . . . Petroleum Thinner............................ Total Ingredients Pliolitc S-5 Base 1............................ Pliolite S-5 Base 13............................ Pliolite S-5 Base 38............................ Pliolite S-5 Base 39............................ Pliolite Base 46.................................... Pliolite Base 46B............................ ... Aroclor 1254........................................ Drying Oil*........................................ High Flash Aromatic Naphtha . . . Petroleum Thinner ........ Total Ingredients Pliolite S-5 Base 7C........................................ Pliolite S-5 Base 13.................... .... Pliolite S-5 Base 38........................................ Pliolite S-5 Base 46B.................................... Aroclor 1254................................................... Drying Oil*................................................... High Flash Aromatic Naphtha.................... Petroleum Thinner.................................... . Total . . . Raw tung oil, perllla or pale grinding linseed oil. 2Z~f~ Yellow Orange Percent by Weight . 20.00 .-- . 25.OO .-- . 1.80 . O.9O . 26.15 . 26.15 23.68 2.79 16.71 4.18 1.78 0.90 25.00 25.00 . 100.00 100.00 Chinese Red Dark Blue Percent by Weight .-- . 21.40 .-- . 26.30 i-54 . 0.76 . 25.00 . 25.00 3.00 21.50 21.50 -- 2.65 1-35 25.00 25.00 . 100.00 100.00 Green Light Gray Percent by Weight . 1.20 . 20.45 ,-- . 20.21 .-- . 0.12 . 242 . 1.20 . 27.20 . 27.20 22.25 18.11 0.65 0.28 0.32 -- 146 0.73 28.10 28.10 . 100.00 100.00 Brown Black Percent by Weight . 5-19 . 11.83 2945 . o.ir -- 26.28 -- 15.76 . 1.89 - 6.95 25-29 25.29 1.84 0.92 27.60 27.60 . 100.00 100.00 t DSW 150445 STLCOPCB4039886 Ingredients Battleship Gray Silver Gray Percent by Weight Pliolite S-5 Base iA.................................................................................... Pliolite S-5 Base 7C...................................................................................... Pliolite S-5 Base 13...................................................................................... Pliolite S-5 Base 38...................................................................................... Pliolite S-5 Base 39C .................................................................................... Pliolite S-5 Base 46B........................................................................... Aroclor 1254............................................................... Drying Oil*............................................... High Flash Aromatic Naphtha ............................................... Petroleum Thinner....................................................................................... 22.50 0.24 20.52 --0--.85 0.96 1.69 0.84 26.20 26.20 23-940 -- 21.840 1.191 O.029 0-153 1.770 0.885 25.096 Total............................................................ 100.00 100.000 The above concrete enamels represent only a few of the colors attainable in Pliolite S-5 Base paints. Paint manufacturers may have their own ideas for arriving at the colors desired and may wish to consult Goodyear for additional information about colors. These paints are considered to have good ultraviolet light resistance and results of accelerated aging tests indicate that they have superior light resistance to competitive products such as oleoresinous concrete enamels. Due to the shortage of titanium dioxide Goodyear have not been able to supply the demand for their Pliolite Base 1-S5. In an effort to relieve this situation, paint manufacturers able to obtain titanium dioxide can prepare concrete floor enamels by wet grinding the titanium dioxide with a three-roll mill or a pebble mill in accordance with the following formulations and procedures: Battleship Gray Concrete Floor Enamel White Base (Three-roll or five-roll mill grind) Percent by Weight Pliolite S-5 Resin Solution1........................................................................................... Aroclor 1254....................................... Drying Oil5...................................................................................................... High Flash Aromatic Naphtha....................................................................................... Petroleum Thinner................................................................... 26.32 6.32 3.16 2.10 2.10 Titanium Dioxide.................................................................................................. 60.00 Total ........................................................................... 100.00 'Pliolite S-s Resin................................... 40% High Flash Naphtha ...............................................30% Petroleum Thinner .................................................. 30% Total..........................................100% 'Raw tung, perilla or pale grinding linieed oil. Run the above white base to a fine grind on a three-roll or five-roll mill. To prepare the finished enamel dissolve the Pliolite S-5 Bases given in the following formula in the given solvents. Then add the roll mill ground White Base and Aroclor plasticizer as given below: Finished Enamel Percent by Weight White Base (Roll Mill Ground)....................................................................................... Pliolite S-5 Base 7C................................ .............................................................. .... Pliolite S-5 Base 13........................................................................................................... Pliolite S-5 Base 38........................................................................................................... Pliolite S-5 Base 46B................................................................................................... Pliolite S-5 Resin....................................... Aroclor 1254 ........................................................................................................ Drying Oil............................................................................................... High Flash Aromatic Naphtha ....................................................................................... 24.40 0.24 20.52 0.85 0.96 5.30 23.75 Petroleum Thinner.......................................................................................................... 23.75 Total........................................................................... 100.00 0.15 0.08 9' -- yy* /O DSW 150446 STLCOPCB4039887 If a pebble mill grind is to be made instead of a roll mill grind, then the following formulation and procedure should be used: White Base Battleship Gray Concrete Floor Enamel (Pebble Mill Grind) Percent by Weight Pliolitc S-s Resin................... Aroclor 1254....................................................................................................................... Drying Oil*....................................................................................................................... High Flash Aromatic Naphtha....................................................................................... Petroleum Thinner....................................................................... Titanium Dioxide........................... 13.52 4.52 2.26 20.30 20.30 39.10 Total ............................................................................ 100.00 Run the above White Base to a fine grind in the pebble mill. To prepare the finished enamel dissolve the Pliolitc S-5 Bases indicated in the following formula in the given solvents. Then add foe pebble mill ground White Base and Aroclor plasticizer as given below: Finished Enamel Percent by Weight White Base (Pebble Mill Ground)................................................................... ... . Pliolite S-5 Base 7C........................................................................................................... Pliolitc S-5 Base 13........................................................................................................... Pliolite S-5 Base 38........................................................................................................... Pliolite S-5 Base 46B....................................................................................................... Pliolite S-5 Resin............................................................................................................... High Flash Aromatic Naphtha............................................................................................. Petroleum Thinner................................................................................................................. 37.39 0.24 20.52 0.85 0.96 2.82 18.61 18.61 Total........................................................................... 100.00 If desired, this enamel may be produced entirely in foe pebble mill by first grinding foe White Base to the required fineness and then adding the balance ofthe materials and continuing the grind to accom plish foe final solution. It is indicated by Goodyear that these latter procedures are applicable in preparing their following types of Pliolite paints: S-102-100 . . . . S-I02-200 .... S-I02-600 .... S-I02-603 .... S-IO2-604 . . . . S-IO2-605 .... S-i02-700 , . . . Prior to giving consideration to foe use ofthese methods or modifications ofthem for other color enamels it is suggested that Goodyear should be consulted for more specific information about their suitability' The following are typical examples of arid and alkali resistant coatings, fume resistant enamel and an aluminum paint vehicle: Acid and Alkali R*ai*tant Coating Black Ingredients Percent by Weight Pliolite S-5 Base 13........................................................................................................... Pliolite S-J Base 46B.......................................................................... 26.28 15.76 Aroclor 1254....................................................................................................................... Drying Oil*...................................................................... High Flash Aromatic Naphtha....................... Petroleum Thinner.............................................................................................. 1.84 0.92 27.60 27.60 Total............................................................................ 100.00 'Raw tung oil, perilla or pale grinding linseed oil, t TSE //"" DSW 150447 STLCOPCB4039888 Fume Reaiatant Enamel Gloss White Ingredients Percent by Wright Pliolite S-5 Base i........................................................................................................... 55.66 Aroclor 1254....................................................................................................................... 1.96 Drying Oil*....................................................................................................................... 0.98 High Flash Aromatic Naphtha....................................................................................... 20.70 Petroleum Thinner ........................................................................................................... 20.70 Total....................................................... 100.00 * Raw tung oil, pcrilla or pale grinding linseed oil. Ingredients Aluminum Vehicle Percent by Weight Pliolite S-5 Resin............................................................................................................... 15.0 Aroclor 5460....................................................................................................................... 15.0 Xylol................................................................... 70.0 Total........................................................................... roo.o The specific properties of this vehicle are: Specific Gravity................................................................... 0.955 Weight per Gallon........................................................... 7.95 lbs. Solids Content....................................................................... 30.0% Viscosity, No. 4 Ford Cup................ ...........................22 seconds To prepare an aluminum finish add No. 422 Alcoa aluminum powder, or equivalent, to the above vehicle in the proportion of 12 percent by weight or 0.95 pounds per gallon. Goodyear indicate that this aluminum paint has very good stability and samples aged in the laboratory for more than two months showed no loss in leafing. If a more flexible finish is desired, liquid or plasti cizer type Aroclors 1242 or 1254 should be used. Piiolito Base 19 S-5 for Imparting Non-Sagging and Improved Brushability to Pliolite S-5 Enamels Goodyear report that difficulties with sagging and brushability of Pliolite S-5 enamels and flat whites have been experienced by some paint firms. To overcome this, it is suggested that Steatite (a special grade of talc) be incorporated in Pliolite S-5 on a two-roll mill to give a base which can be used to pre vent sagging and improve the brushability of Pliolite S-5 formulations. Goodyear offer this base, con taining 70 percent of Steatite and 30 percent of Pliolite S-5 under their trade name Pliolite Base 19 S-5. Addition of this base to Pliolite S-5 formulations tends to prevent sagging, improve brushing, prevent hard settling, impart high thixotropic consistency in solution and effect gloss only slightly. Description of Pliolite Base 19 S-5 Composition........................................................30% Pliolite S-5 70% Steatite Specific gravity........................................................................ 1.91 Gloss of film............................................................... Satin sheen Color of film............................................ Semi-transparent, milky EFFECT OF PLIOLITE BASE 19 S-5 ON PLIOLITE S-5 ENAMELS The following formulations illustrate the results obtained by incorporating Pliolite Base 19 S-5 in Pliolite S-5 enamels. For example, die following Formula No. 1 demonstrates the results obtained by the addition of an aged solution of Pliolite Base 19 S-5 to a Pliolite S-5 enamel. --11 -- ~T7~~ tL DSW 150448 STLCOPCB4039889 Formula No. 1 To one gallon of Pliolite S-5 gloss white enamel containing: Ingredients Pliolite Base 1 S-5................................................................... Aroclor 1254............................................................................... Dicing Oil................................................................................... High Flash Aromatic Naphtha................................................ Petroleum Thinner................................................................... Total.................................... Percent by Weigh; 55.66 1.96 0.98 20.70 20.70 100.00 Add 28 ounces of an aged solution of: Ingredients Pliolite Base 19 S-5................................................................... High Flash Aromatic Naphtha................................................ Petroleum Thinner................................................................... Total.................................... Percent by Weight . 40.0 30.0 30-Q . 100.0 The following Formula No. 2 demonstrates the results obtained by dissolving the Pliolite 19 S-5 along with the other ingredients of the enamel. Formula No. 2 Ingredients Percent by Weight Pliolite Base 1 S-5................................... Pliolite Base 19 S-5........................................... Aroclor 1254....................................................................................................................... 45.05 7.00 1.80 Drying Oil........................................................................................................................... High Flash Aromatic Naphtha....................................................................................... 0.90 22.63 Petroleum Thinner........................................................................................................... 22.63 Total........................................................................... 100.00 Formula No. 3 (Control) Formula No. 3 is identical with Formula No. 1 with the exception that the Pliolite Base 19 S-5 has been omitted. It serves as a control in the following comparative study in which the viscosity and consistency of the enamels are given. Formula No. 1 No. 2 No. 3 No. 4 Ford Cup 275 sec. 208 sec. 118 sec. Stormer 47 sec. 40 sec. 27 sec. Solid Content 55.9% 54-7% 58.6% Stormer consistency is given in seconds per loo revolutions of a forked rotor with a 200 g. weight. Both Formulas No. 1 and No. 2 contain about 0.5 pounds of Steatite per gallon. Although their solids content is lower than that of Formula No. 3, their consistency is substantially higher. This illustrates that Pliolite Base 19 S-5 adds body to the enamel and in actual brushouts both Formulas No. 1 and No. 2 were much better in working qualities than Formula No. 3 and showed no evidence of sagging. VI. DRYING RATE OF AROCLOR PLASTICIZED PLIOLITE S-5 FORMULATIONS Many of the Aroclor plasticized Pliolite S-5 enamels dry tack free in less than one hour. However' in common with other paint materials these enamels require several days to reach maximum hatdness. Since drying and the development of hardness, in the case of these paints, are due only to solvent removal, force drying at elevated temperatures to accelerate the rate of solvent removal increases drying to a marked degree. The rate of drying, especially to the tack free condition, can be varied in accordance with the evapora tion rate of selected solvents. The diying rate of the enamels increases with increased pigment and filler content. Drying oils added to the enamels increase the time required to attain maximum hardness. The incorpo ration of Aroclor plasticizers tends to reduce the time required for maximum hardness to develop. -- 12 -- JZET A3 DSW 150449 VII. PLASTICIZERS AND MODIFYING AGENTS IN ADDITION TO AROCLORS OF INTEREST IN PLIOLITE S-S PAINTS C-- Clear film; complete compatibility H -- Hazy film I -- Cloudy am; incompatible Material Drying Oils llDrisoy"A"............................ .... "Drisoy "B"............................ .... "KelX-L.................................... . . . . Linseed, high arid................ . . . . Linseed, neutral.................... "Diamond K Linseed .... . . . . Oitidca.................................... . . . . Perilla.................................... ... Soya, alkali refined................ 'Thermolized Tung................ Tung, raw . ............................ .... .... .... .... 5:100 si. H si. H si. H C H C C I si, H C Ratio to Pliolite Resin 10:100 25:100 HI HI HI CH CH I HH HI --,, HI CC 50:100 I I I -- -- H Chemical Plasticizers AROCLORS, chlorinated biphenyl and chlorinated polyphenyls (all grades) , C c c c Chlorinated paraffin................................ C c c c Diamyl naphthalene................................ c c c c Dibutyl plithalate.................................... c c c c Dioctyl phthalate.................................... c c c c Hercolyn................................................ c c c c Kapsol.................................................... c c c c Rronisol.................................................... c c c c *KP-23................................................... c c c c Methox.................................................... c c c c MONSANTO'S SANTICIZER B-16. c c c c Tricresyl phosphate............................ ... c c c c Resina AROCLORS, chlorinated biphenyl and chlorinated polyphenyls (all grades) . Cumar (all grades)................................ wDuraplex AL-2J0-L................................ Durex No. 220........................ ... Ester gum................................................ Limed rosin............................................ `Pentalyn A................................................ `Pentalyn G................................................ Pentalyn M............................................ Pentalyn X............................................ Polystyrene............................................ Rosin........................................................ Staybelite Ester No. 10........................ Zinar....................................................... 'Zirex....................................................... C C H C C c c c si. H C I c c c c ccc ccc H I-- ccc c cc cHH ccc c c si. H H I-- c 1-- ------ ccc ccc c I --* ccc Vamiahes Linseed-Cumar, 12)^ gal........................ Linseed-Cumar, 25 gal............................. c c c c cc I-- Linseed-Araberol ST-137,12X gal- c c 1-- -13- , JSZ7 )</- DSW 150450 STLCOPCB4039891 Material Miscellaneous Acrylic resins........................................ Alkyd resins............................................ Buna-Nj synthetic rubber.................... Cellulose Nitrate.................................... Coumarone-indene oils and resins . . . Gilsonite. ................................................ Gloss Oil N-Glo-5y................................ "Gloss Oil................................................ GR-S, synthetic rubber . ................. 1 Lecithin Yelkin TTS............................ Maleic resins............................................ Phenolic resins........................................ Piccolastic B ioo.................................... Polyvinylchloride.................................... Rosin Oil ................................................ 5:100 Ratio to Pliolite Resin 10:100 25:100 50:100 I Ma Alkyd resins as a class are not compatible. I ---- --* I-- -- mmm CCcc I-- -- -- CcH I C c CH HHHH H I-- -- Maleic resins as a class are not compatible. Phenolic resins as a class are of limited compatibility. CcCc I *>* -- Cccc SUPPLIERS American Lecithin Company, Inc. Barrett Division, Allied Chemical and Dye Corporation Durez Plastics and Chemicals, Inc. Hercules Powder Company `Newport Industries, Inc. 70`Bnen Varnish Company Ohio-Apex, Inc. Pennsylvania Industrial Chemical Corp. `"The Resinous Products and Chemical Company "Spencer Kellogg and Sons, Inc. . VIII. GENERAL The principal applications for Pliolite S-5 paints plasticized with Aroclors are coatings for metal, con crete, brick and masonry surfaces requiring resistance to adds, alkalies, water and other corrosive influences. These enamels are suggested for use as concrete floor paints, architectural finishes, metal primers and finishes, oil and grease-resistant coatings, baking primers and enamels, corrosion-resistant coatings and ship bottom paints. Arodors have a pronounced plastidzing action on Pliolite S-5 (butadiene and styrene co-polymer) imparting flexibility to the paint coatings and increasing their life. The formulations of Arodors and Pliolite S-5 along with their suggested uses, as given in this report, are in line with good commerdal practice. Much of the information given was obtained from other firms, particularly Goodyear Tire and Rubber Company, Chemical Products Division, Akron, Ohio. The data given is to serve as a guide or starting point in the development offormulations to expand taking advantage of the outstanding qualities of Arodors as plastidzers and resins for Pliolite S-5 paints. The information contained in this bulletin is to our best knowledge true and accurate, but all recom mendations or suggestions are made without guarantee, since the conditions ofuse are beyond our control. Monsanto Chemical Company disdaims any liability incurred in connection with the use of these data or suggestions. Furthermore, nothing contained herein shall be construed as a recommendation to use any product in conflict with existing patents covering any material or its use. MONSANTO CHEMICAL COMPANY Saint Louis 4, Missouri New York < Chicago - Boston - Birmingham Charlotte Cincinnati Philadelphia Detroit * Los Angeles San Francisco Montreal POI-rti 2M~71 frlMtSInU.S.A. rzzvs"11- DSW 150451 STLCOPCB4039892 Monsanto Chemicals __ kA__ For further information about Aroclors at used in Pliolite S-5, write, wire or call the nearest Monsanto office. MONSANTO CHEMICAL COMPANY ST. LOUIS AKRON . BIRMINGHAM BOSTON CHARLOTTE * CHICAGO CINCINNATI . CLEVELAND DETROIT HOUSTON LOS ANGELES NEW YORK PHILADELPHIA SAN FRANCISCO SEATTLE MONSANTO (CANADA) LTD. MONSANTO (AUSTRALIA) FTY LTD. Montreal Toronto Vancouver Melbourne MONSANTO CHEMICALS LTD. London Representatives in the Principal Cities of the World. DSW 150452 STLCOPCB4039893