Attached in Table I is a sunmary of residual VCM levels in suspension vinyl resins produced during the month of August. A slight increase in VCM content of QSQH-7 production was noted as compared to the previous production in June. A slight decrease in VCM content of VSJE-10 was also noted*
Individual bin and blend VCM data for each suspension type produced during the month are shown in Tables II-VIII. Also shown in Tables IX and X are residual VCM levels in VYNW/QYNL and VYDS blends, respectively, which were produced during the month. All solvent bins produced since the unit start-up in mid-August analyzed <1 ppm, as did all VYDS blends produced during the month.
/kw Attachments
RESINS LABORATORIES UNION CARBIDE CORPORATION CHEMICALS AND PLASTICS DIVISION
TEXAS CITY PLANT
UCC
038821
TABLE I SUMMARY OF VCM ANALYSIS OF SUSPENSION VINYL RESINS
Resin Type
QSAN-7 QSQH-7 VSJE-10
VCM, ppm
Bin Blend
381 244
425 171
1141
479
% VCM Reduction % Biends <100 ppm from Blending
44 36 63 60
0 58
UCC
038822
TABLE II
QSAN-7 BLEND ANALYSIS FOR VCM CONTENT
Blend Number B-6374 B-6377 B-6378 B-6379 B-6380 B-6381 B-6382 B-6383 B-6384
Date 8-10 8-13 8-18 8-17 8-15 8-15 8-18 8-15 8-18
VCM, pi 270
1386 173 32 <1 78 134 16 107
UCC
038823
TABLE III
QSQF BLEND ANALYSIS FOR VCM CONTENT
B1end Number B-328 B-330 B-331 B-332
Date 8-1 8-1 8-1 8-4
VCM, ppm 85
394 43
455
UCC
038824
TABLE IV
QSQH-7 BLEND ANALYSIS FOR VCM CONTENT
Blend Number
B-933 B-934 B-935 B-936 B-937 B-938 B-939 B-940 B-941 B-942 B-943 B-944 B-945 B-946 B-947 B-948 B-949 B-950 B-951 B-953 B-954 B-955 B-956 B-957 B-958 B-959 B-960 B-961 B-962 B-963
Date
8-3 8-3 8-3 8-5 8-3 8-3 8-3 8-5 8-5 8-6 8-6 8-7 8-8 8-7 8-8 8-11 8-11 8-10 8-11 8-11 8-13 8-13 8-14 8-14 8-15 8-18 8-18 8-18 8-18 8-27
VCM, pi
120 1147
109 42
1106 44 88 23 38 69 99 51 22 54 508 26 66
140 292
82 48 27 120 58 165 111 35 363 26 44
ucc
038325
TABLE V
VSJE-10 BLEND ANALYSIS FOR VCM CONTENT
Blend Number
B-776 B-783 B-785 B-786 B-788 B-789 B-790 B-791 B-792 B-793 B-794 B-795 B-797
Date
8-1 8-1 8-1 8-1 8-1 8-1 8-5 8-3 8-3 8-3 8-5 8-5 8-5
VCM, pi
346 545 555 566 519 590 417 291 466 572 563 586 446
ucc
038826
TABLE VI
QSAN-7 BIN ANALYSIS FOR VCM CONTENT
Bin Number
703 702 706 402 708 701 704 704 701 709 702 706 708 703
Date
8-6 8-8 8-7 8-7 8-8 8-10 8-10 8-12 8-12 8-14 8-15 8-15 8-14 8-15
VCM, ppm
539 1001
427 5
1148 552 618 70 21 72 41 171 395 274
ucc
038827
TABLE VII
QSQH-7 BIN ANALYSIS FOR VCM CONTENT
i Number
604 602 606 606 603 601 606 606 602 601 606 603 604 608 609 601 608 606 601 607 601 602 609 608 606
Date
8-2 8-2 8-2 8-1 8-2 8-1 8-1 8-3 8-4 8-3 8-5 8-4 8-6 8-8 8-8 8-10 8-9 8-10 8-12 8-12 8-13 8-13 8-14 8-15 8-16
VCM, pi
1631 515 144 157 175
3674 194 209 252 142 214 159 113 407 471 298 289 286 101 52 16 171 406 211 335
UCC
038828
TABLE VIII
VSJE-10 BIN ANALYSIS FOR VCM CONTENT
Bin Number 709 701 704 708 706 702 706 705 708 704
Date 8-1 8-2 8-1 8-2 8-2 8-3 8-4 8-3 8-3 8-4
VCM, ppn 899 1570
1211 1360
969 1060 1244 1103 1280 709
UCC 038829
TABLE IX
QYNL/VYNW BLEND ANALYSIS FOR VCM CONTENT
VYNW QYNL
Blend Number B-3883 B-3884 B-3885
B-1452 B-1453 B-1454 B-1455
Date 8-20 8-16 8-16
8-3 8-8 8-8 8-15
VCM, ppm 9.8 1.7 1.7
2.2 0.6 <0.5 <0.5
UCC 038830
TABLE X
VYDS BLEND ANALYSIS FOR VCM CONTENT
Type Regular Rule 66 Regular Rule 66 Regular Regular Regular
Blend Number B-775 B-776 B-777 B-778 B-779 B-780 B-781
VCM, ppf 0.30
<0.2 <0.2 <0.2 <0.2 <0.2
0.50
UCC
038831
DISTRIBUTION
TEXAS CITY PLANT
Dr. J. C. Chaty/Dr. D. R. Montgomery Mr. M. E. Eisenhour Mr. R. L. Frantz Mr. F. L. Johnson Mr. K. E. Ross Mr. R. W. Sesler
BOUND BROOK PLANT Mr. E. Bell
NEW YORK OFFICE Mr. G. P. Bigelow Mr. D. E. Hardman Mr. G. T. Scott Dr. A. B. Steele Or. T. T. Szabo Mr. A. E. Donaldson
SOUTH CHARLESTON PLANT ^ Mr. R. N. Wheeler
TECHNICAL CENTER Dr. J. J. Brezinski
UCC 03883^