Document 3e7x3NJ3N0v0ogELVeeNO7KKD

Attachment-3List of properties 1.Plastics Plastic type Formability Physical properties Mechanical properties Thermal properties Electrical properties Other chemical property Formability Compression molding temperature Injection molding temperature Mold shrinkage rate Specific gravity Water absorption rate (24 -3 .18mm thickness ) Tensile strength MPa Elongation Tensile modulus of elasticity MPa Compressive strength MPa Flexural strength MPa Impact strength(Izod/notch)J/m Hardness (Rockwell) Coefficient of thermal expansion 105/ Continuous heat resistance temperature Melting point Deflection temperature under load (1 .81MPa) Volume resistance (50% , RH23) Dielectric breakdown strength Short-time Permittivity 103Hz(106Hz) Arc resistance sec Burning rate mm/min Effects of weak acids Effect of strong acid Effects of weak alkali Effect of strong alkali - D792 D570 D638/651 D638 D638 D638 D638 D638 D785 D696 D2117 D648 D257 D149 D150 D495 D635 D543 D543 D543 D543 Organic solvent resistance D543 Polytetrafluoroethylene PTFE 2 .13 - 2 .20 0 .01 20 - 35 200 - 400 10-15 150 - 160 R20 10 260 327 55 1018 19 2 .1 300 V-0 Fluorinated-ethylenepropylene FEP 319 - 399 329 - 404 3 .0 - 6 .0 2 .12 - 2 .17 0 .01 20 - 35 300 - 350 15 - 20 didn't break R50 12 260 310 47 1018 20 2 .1 300 V-0 Perfluoroalkoxy alkane PFA 329 - 371 371 - 427 2-3 2 .15 - 2 .17 0 .01 20 - 30 200 - 400 14 - 19 didn't break R50 9 200 260 50 1018 22 2 .1 300 V-0 Regulated materials Polychlorotrifluoroethylene PCTFE Ethylene tetrafluoroethylene ETFE 238 - 254 227 - 316 1 .0 - 1 .5 2 .10 - 2 .20 1 .73 - 1 .74 0 .01 0 .03 31 - 41 80 - 250 31 - 51 135 - 145 R80 38 - 42 300 - 400 40 - 50 didn't break R50 6 6 120 220 90 1018 22 2 .6 300 V-0 150 270 74 1017 16 2 .6 75 V-0 Ethylenechlorotrifluoroethylene ECTFE 1 .68 - 1 .69 0 .01 41 - 48 200 - 300 35 - 40 didn't break R50 8 150 245 77 1015 20 2 .6 18 V-0 Polyvinylidene fluoride PVDF 204 - 288 232 - 288 3 1 .75 - 1 .78 0 .03 30 - 70 200 - 370 32 - 74 160 - 375 R93 - 116 16 150 151 - 178 100 1015 11 8 .4 60 V-0 Plastic type Formability Formability Compression molding temperature Injection molding temperature Mold shrinkage rate Physical properties Specific gravity Water absorption rate (24 -3 .18mm ) Tensile strength /2 Elongation Mechanical properties Tensile modulus of elasticity 104kg/ Compressive strength /2 Flexural strength /2 Impact strength(Izod/notch)J/m Hardness (Rockwell) Thermal properties Electrical properties Coefficient of thermal expansion 105/ Continuous heat resistance temperature Heat deformation temperature (18 .5Kg/2) Volume resistance (50% , RH23) Dielectric breakdown strength Short-time Permittivity 103 Arc resistance sec Other Burning rate (flame resistance) Effects of weak acids Effect of strong acid chemical property Effects of weak alkali Effect of strong alkali Organic solvent resistance ECHA alternative candidate Polyvinyl chloride PVC Hard PVC Soft High density polyethylene HDPE - - - 141 - 204 141 - 177 149 - 232 D792 D570 149 - 204 0 .1 - 0 .5 1 .35 - 1 .45 0 .07 - 0 .40 160 - 195 1-5 1 .16 - 1 .35 0 .15 - 0 .75 149 - 316 2-5 0 .94 - 0 .97 0 .01 D 638/651 D 638 D 638 350 - 630 2 - 40 2 .5 - 4 .2 105 - 630 200 - 450 - 220 - 390 15 - 100 0 .42 - 1 .1 D 695 D 790 D 256 D 785 D 696 560 - 910 700 - 1130 2 .2 - 109 70 - 90 ( Shore D) 5 - 18 .5 63 - 120 - 50 - 100 ( Shore A ) 7-25 230 70 8 .2 - 10 .9 60 - 70 ( Shore D) 11-13 - 66 - 79 66 - 79 121 D 648 D 257 D 149 54 - 74 1016 16 .7 - 51 .1 1011 - 1015 11 .8 - 39 .3 43 - 54 1016 17 .7 - 19 .7 D 150 D 495 3 - 3 .3 60 - 80 4-8 2 .3 - 2 .35 - - D 635 Self-extinguishing Slow self-extinguishing Very slow D 543 D 543 D 543 D 543 D 543 - Swelling or soluble in ketones, esters, swelling in aromatics. - Swelling or soluble in ketones, esters, swelling in aromatics. Withstand (80C or less) Low density polyethylene LDPE 135 - 177 149 - 371 1 .5 - 5 .0 0 .91 - 0 .93 0 .015 70 - 160 90 - 800 0 .11 - 0 .25 didn't break 41 - 46 ( Shore D) 16 - 18 82 - 100 32 - 40 1016 18 .1 - 27 . 5 2 .25 - 2 .35 135 - 160 Very slow Withstand (80C or less) Polypropylene 171 - 232 199 - 304 1 - 2 .5 0 .90 - 0 .91 0 .01 300 - 390 200 - 700 1 .1 - 1 .4 420 - 560 420 - 560 3 .3 - 33 85 - 110 6 - 8 .5 107 - 150 52 - 60 1016 19 .7 - 26 2 .2 - 2 .3 185 Slow Withstand (80C or less) Polyvinyl fluoride PVF 1 .33 82 140 100 203 1013 8 .4 Poly phenylene sulfide PPS 1 .34 0 .02 81 8 132 4 - 2 .4/2 .9 278 260 1 1014 30 3 .5 V-0 Poly ether ether ketone PEEK - 1 0 105 22 174 6 M99 4 ECHA alternative candidates Polyamide 66 PA66 - - 280-300 0.8-1.5 1.07-1.09 1.0-1.3 48-67 55-200 59 907-1014 R100 (dry)R107, 113 - modifiedPolyphenyleneether m-PPE - 240 - 270 220 - 350 0.5 - 0.7 1.04 - 1.09 0.06 - 0.12 66 60 2,500 - 2,600 113 66 - 96 267 R118 - 120 3.3 - 7.7 Polybutylene terephthalate PBT - 220-270 1.5-2.0 1.30-1.38 0.08-0.09 57 50-300 1,900-3,000 59-100 82-115 37-53 M68-78 6.0-9.5 343 156 5 1016 260 66-68 1011-1014 107 - 149 1017 224 50-85 1015-1016 - - 20 - 28 17-22 3 - 2.6 (3.1-3.3) - 130-140 75 75-192 V-0 Self-extinguishing Self-extinguishing Dissolved in phenol/formic Swells or dissolves in acid aromatic and chlorinated Swells in polar solvents hydrocarbons 2.Elastomers Elastomer type Mechanical properties physical properties Electrical properties Oil and chemical resistance Specific gravity of pure rubber JIS hardness range possible Tensile strength (/) Elongation Rebound resilience tear strength Compression set Wear resistance Flex-crack resistance Heat resistance (maximum specified temperature ) Cold resistance (brittleness temperature C) Aging resistance Ozone resistance Light (weather) resistance Flame resistance Gas permeability cccm/cmsecatm Radiation resistance Volume resistivity / Breakdown voltage (V/mil,Short time) Permittivity Gasoline/light oil Benzene/Toluene Trichlene Alcohol Ether Ketone () Ethyl acetate Water Organic acid High concentration inorganic acid low concentration inorganic acid High concentration alkali Low concentration alkali D 297 K 6301 K 6301 K 6301 K 6301 K 6301 D 394 746 K 6301 518 257 D 149 150 K 6301 K 6301 K 6301 Regulated materials Fluoro rubber(Viton) FKM FPM 1.80-1.82 50-90 70-200 100-500 300 10-50 1 - 1015-1018 450-600 2.0-2.5 - Nitrile rubber NBR 1.00-1.20 15-100 50-250 100-800 130 10-20 - 0.3-3.5 - 109-1010 500 15-20 - - - - ECHA alternative candidate Ethylene/Propylene Rubber EPM EP EPDM Acrylic rubber ACM ANM 0.86-0.87 1.09-1.10 30-90 40-90 50-200 100-800 70-120 100-600 150 180 40-60 15 1012-1015 1000-1500 3.1-3.4 0-30 - 10 - 108-1010 Silicone rubber Si Q VMQ SR 0.95-0.98 30-90 40-100 50-500 - - - 280 70-120 - 400 - 1011-1015 500-1100 3.2-10.0 - - - - -